Hot Rolled Stainless Steel Sheet SUS 430 Gauge 8 for Industrial and
Construction Needs
Hot rolled stainless steel plates are produced through a process
where the steel is heated above its recrystallization temperature
and then passed through rollers to achieve the desired thickness
and surface finish.
Product introduction:
| Commodity | Hot Rolled Stainless Steel Sheet SUS 430 Gauge 8 for Industrial and
Construction Needs |
| Grade | 430 |
| Brand | TISCO ,BAOSTEEL,POSCO,JISCO,LISCO |
| Certification | SGS,BV,IQI,TUV,ISO,etc |
| Thickness | 4.191 mm |
| Width | 1500 mm |
| Length | 3000 mm |
| Surface | NO.1/NO.3/NO.4/8K/HL/2D/1D |
| Standard | JIS,AISI,ASTM,GB,DIN |
| Delivery time | About 15 -30 days or based on the sales contract |
| MOQ | 1 Ton |
| Advantages | Showing the splendor of your quality, wear resistant as well , Strong corrosion resistance and decorative effect, durable and
beautiful in good taste. |
Brand Cross Reference Table:
| GB NEW BRAND | JIS | ASTM | UNS | KS | BS EN | AS |
| 12Cr17Mn6Ni5N | SUS201 | 201 | S20100 | STS201 | 1.4372 | 201-2 |
| 12Cr18Mn9Ni5N | SUS202 | 202 | S20200 | STS202 | 1.4373 | - |
| 12Cr17Ni7 | SUS301 | 301 | S30100 | STS301 | 1.4319 | 301 |
| 06Cr19Ni10 | SUS304 | 304 | S30400 | STS304 | 1.4301 | 304 |
| 022Cr19Ni10 | SUS304L | 304L | S30403 | STS304L | 1.4306 | 304L |
| 06Cr19Ni10N | SUS304N1 | 304N | S30451 | STS304N1 | 1.4315 | 304N1 |
| 06Cr19Ni9NbN | SUS304N2 | XM21 | S30452 | STS304N2 | - | 304N2 |
| 022Cr19Ni10N | SUS304LN | 304LN | S30453 | STS304LN | - | 304LN |
| 10Cr18Ni12 | SUS305 | 305 | S30500 | STS305 | 1.4303 | 305 |
| 06Cr23Ni13 | SUS309S | 309S | S30908 | STS309S | 1.4833 | 309S |
| 06Cr25Ni20 | SUS310S | 310S | S31008 | STS310S | 1.4845 | 310S |
| 06Cr17Ni12Mo2 | SUS316 | 3016 | S31600 | STS316 | 1.4401 | 316 |
| 06Cr17Ni12Mo2Ti | SUS316Ti | 316Ti | S31635 | - | 1.4571 | 316Ti |
| 022Cr17Ni12Mo2 | SUS316L | 316L | S31603 | STS316L | 1.4404 | 316L |
| 06Cr17Ni12Mo2N | SUS316N | 316N | S31651 | STS316N | - | 316N |
| 022Cr17Ni13Mo2N | SUS316LN | 316LN | S31653 | STS316LN | 1.4429 | 316LN |
| 06Cr18Ni12Mo2Cu2 | SUS316J1 | - | - | STS316J1 | - | 316J1 |
| 022Cr18Ni14Mo2Cu2 | SUS316J1L | - | - | STS316J1L | - | - |
| 06Cr19Ni13Mo3 | SUS317 | 317 | S31700 | STS317 | - | 317 |
| 022Cr19Ni13Mo3 | SUS317L | 317L | S31703 | STS317L | 1.4438 | 317L |
| 06Cr18Ni11Tji | SUS321 | 321 | S32100 | STS321 | 1.4541 | 321 |
| 06Cr18Ni11Nb | SUS347 | 347 | S34700 | STS347 | 1.455 | 347 |
| 12Cr13 | SUS410 | 410 | S41000 | STS410 | 1.4006 | 410 |
| 20Cr13 | SUS420J1 | 420 | S42000 | STS420J1 | 1.4021 | 420 |
| 10Cr17 | SUS430 | 430 | S43000 | STS430 | 1.4016 | 430 |
Gauge and Inch:
| Gauge | SS inch | SS mm | Mild Steel | Galvanized Steel |
| | | | |
| 3 | 0.25 | 6.35 | 0.2391 | |
| 4 | 0.2344 | 5.95376 | 0.2242 | |
| 5 | 0.2187 | 5.55498 | 0.2092 | |
| 6 | 0.2031 | 5.15874 | 0.1943 | |
| 7 | 0.1875 | 4.7625 | 0.1793 | |
| 8 | 0.165 | 4.191 | 0.1644 | 0.168 |
| 9 | 0.1562 | 3.96748 | 0.1495 | 0.1532 |
| 10 | 0.1406 | 3.57124 | 0.1345 | 0.1382 |
| 11 | 0.125 | 3.175 | 0.1196 | 0.1233 |
| 12 | 0.1094 | 2.77876 | 0.1046 | 0.1084 |
| 13 | 0.0937 | 2.37998 | 0.0897 | 0.0934 |
| 14 | 0.0781 | 1.98374 | 0.0747 | 0.0785 |
| 15 | 0.0703 | 1.78562 | 0.0673 | 0.071 |
| 16 | 0.0625 | 1.5875 | 0.0598 | 0.0635 |
| 17 | 0.0562 | 1.42748 | 0.0538 | 0.0575 |
| 18 | 0.05 | 1.27 | 0.0478 | 0.0516 |
| 19 | 0.0437 | 1.10998 | 0.0418 | 0.0456 |
| 20 | 0.0375 | 0.9525 | 0.0359 | 0.0396 |
| 21 | 0.0344 | 0.87376 | 0.0329 | 0.0366 |
| 22 | 0.0312 | 0.79248 | 0.0299 | 0.0336 |
| 23 | 0.0281 | 0.71374 | 0.0269 | 0.0306 |
| 24 | 0.025 | 0.635 | 0.0239 | 0.0276 |
| 25 | 0.0219 | 0.55626 | 0.0209 | 0.0247 |
Chemical Composition:
| Grade | C | Si | Mn | P | S | Ni | Cr | Mo |
| 201 | ≤0.15 | ≤1.00 | 5.5～7.5 | ≤0.060 | ≤0.03 | 3.5～5.5 | 16.00～18.00 | - |
| 202 | ≤0.15 | ≤1.00 | 7.5～10.0 | ≤0.060 | ≤0.03 | 4.0～6.0 | 17.00～19.00 | - |
| 301 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 6.00～8.00 | 16.00～18.00 | - |
| 302 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.00～10.00 | 17.00～19.00 | - |
| 304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.00～10.00 | 18.00～20.00 | - |
| 304L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 9.00～13.00 | 18.00～20.00 | - |
| 310S | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 19.00～22.00 | 24.00～26.00 | - |
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.00～14.00 | 16.00～18.00 | 2.00～3.00 |
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 12.00～15.00 | 16.00～18.00 | 2.00～3.00 |
| 321 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 9.00～13.00 | 17.00～19.00 | - |
| 410 | ≤0.15 | ≤1.00 | ≤1.00 | ≤0.040 | ≤0.03 | | 11.500～13.50 | - |
| 430 | ≤0.12 | ≤1.00 | ≤1.00 | ≤0.040 | ≤0.03 | | 16.00～18.00 | - |
Physical Property:
| Grade | Tensile Strength(Mpa) | Yield Strength(Mpa) | Elongation(%) | HBW | HRB | HV |
| 304L | ≥480 | ≥175 | ≥40 | ≤187 | ≤90 | ≤200 |
| 304 | ≥520 | ≥205 | ≥40 | ≤187 | ≤90 | ≤200 |
| 304J1 | ≥450 | ≥155 | ≥40 | ≤187 | ≤90 | ≤200 |
| 304N1 | ≥550 | ≥275 | ≥35 | ≤217 | ≤95 | ≤200 |
| 304N2 | ≥690 | ≥345 | ≥35 | ≤248 | ≤100 | ≤260 |
| 316 | ≥520 | ≥205 | ≥40 | ≤187 | ≤90 | ≤200 |
| 316L | ≥480 | ≥175 | ≥40 | ≤187 | ≤90 | ≤200 |
| 321 | ≥520 | ≥205 | ≥40 | ≤187 | ≤90 | ≤200 |
| 409L | ≥360 | ≥175 | ≥25 | ≤162 | ≤80 | ≤175 |
| 410L | ≥360 | ≥195 | ≥22 | ≤183 | ≤88 | ≤200 |
| 430 | ≥450 | ≥205 | ≥22 | ≤183 | ≤88 | ≤200 |
| 430J1L | ≥390 | ≥205 | ≥22 | ≤192 | ≤90 | ≤200 |
| 436L | ≥410 | ≥245 | ≥20 | ≤217 | ≤96 | ≤230 |
| 410 | ≥440 | ≥205 | ≥20 | ≤201 | ≤93 | ≤210 |
| 201 | ≥520 | ≥275 | ≥55 | ≤241 | ≤100 | ≤253 |
| 202 | ≥520 | ≥275 | ≥55 | ≤207 | ≤95 | ≤218 |
Uses:
Used in welding and boiler making, hot rolled steel is ideal to
construct materials such as railroad tracks and l-beams. Another
advantage of hot rolled steel is that the surface finish of the
product is not an issue. Offering incomparably the best value. All
cutting work could entail a 'slit then shear' method.
Surface Finish:
| Surface Finish | Definition | Application |
| 2B | Finished by heat treatment, pickling after cold rolling. Followed
by skin pass line to be more brighter and smooth surface | General application Medical instruments, Tableware |
| BA | Bright heat treament after cold rolling | Kitchen utensil, kitchenware, architectural |
| 8K | A mirror-like reflective surface by polishing with finer abrasives
over 800mesh | Construction, mirrors, plate sets, decoration elevators |
| HL | Finished by continuous linear polishing | Architectural purpose, Escalators, kitchenware, vehicles |
| NO.1 | Finished by hot rolling, annealing and picking, characterized by
white pickled surface | Chemical industry Equipment, industrail tanks |
| NO.4 | Polishing with NO.150 to NO.180 mesh abrasives specified in
JISR6001 | Kitchen utensils, Building Construction, Medical equipment |
Packing:
Ferrite Stainless Steel Sheet SUS 430 Gauge 8 Hot Rolled 1500x3000 2 types:
l Standard packing
l Fine packing
Factory and Machine Equipment:
We had our own factory to do slitting re-rolling and finish
treatment machine,PVC and interleaving paper we will using with our
machine for you,could protect stainless steel surface from damage
or any scratches,
1. CNC Flame Cutting Machine
2. CNC Plasma Cutting Machine
3. CNC Laser Cutting Machine
4. Bending Machine
5. Shearing Machine
6. Punch Machine
7. Driving Machine
Stainless Steel Sheet 410 BS EN 1.4006 Hot Rolled Plate HR Sheet
Diaplay:
WHY CHOOSE US:
Q1: What is your terms of payment?
A: 30% T/T in advance, the balance 70% before delivery. We will
show you the photos of products and package before you pay the
balance.
Q2: what is the terms of delivery?
A: FOB, CIF, CFR,
Q3: What is the terms of packing?
A: generally, we pack our goods in bundles or coils with rods or
belts, we could also pack the goods as the customers' requirement.
Q4: What is your delivery time?
A: For stocks, we could transport the goods to loading port within
7 days after we received your deposit.
For production period, it usually takes about 15 days-30 days after
receiving the deposit.
Q5: Could you produce according to the samples?
A : Yes, we could customer-made by your samples or technique
drawings, we could build the mold and fixtures.
Q6: Could you provide the samples?
A: yes, we could provide the free samples on conditons it is
available in stocks, however, the the transportation fee is borne
by buyer.