3mm Thickness SUS 304 304L hot rolled steel plate for Oil and Gas
Industry
The materials of hot-rolled plates are usually ordinary carbon
steel, low alloy high-strength steel, stainless steel, etc., which
have high strength and toughness and are suitable for making
various mechanical parts, building structural components, etc.
The production process of hot-rolled plates is relatively simple
and the cost is low, so the price is relatively cheap, making it a
commonly used steel variety.
Product introduction:
| Commodity | 3mm Thickness SUS 304 304L hot rolled steel plate for Oil and Gas
Industry |
| Grade | 304 304L |
| Brand | TISCO ,BAOSTEEL,POSCO,JISCO,LISCO |
| Certification | SGS,BV,IQI,TUV,ISO,etc |
| Thickness | 3 mm |
| Width | 1000 1218 1500 2000 mm |
| Length | 2000 2438 3000 4000 6000 mm |
| Surface | NO.1 |
| Standard | JIS,AISI,ASTM,GB,DIN |
| Delivery time | About 15 -30 days or based on the sales contract |
| MOQ | 1 Ton |
| Advantages | 304 stainless steel is the most common form of stainless steel used
around the world due to excellent corrosion resistance and value |
Brand Cross Reference Table:
| GB NEW BRAND | JIS | ASTM | UNS | KS | BS EN | AS |
| 06Cr19Ni10 | SUS304 | 304 | S30400 | STS304 | 1.4301 | 304 |
| 022Cr19Ni10 | SUS304L | 304L | S30403 | STS304L | 1.4306 | 304L |
Gauge and Inch:
| Gauge | SS inch | SS mm | Mild Steel | Galvanized Steel |
| | | | |
| 3 | 0.25 | 6.35 | 0.2391 | |
| 4 | 0.2344 | 5.95376 | 0.2242 | |
| 5 | 0.2187 | 5.55498 | 0.2092 | |
| 6 | 0.2031 | 5.15874 | 0.1943 | |
| 7 | 0.1875 | 4.7625 | 0.1793 | |
| 8 | 0.165 | 4.191 | 0.1644 | 0.168 |
| 9 | 0.1562 | 3.96748 | 0.1495 | 0.1532 |
| 10 | 0.1406 | 3.57124 | 0.1345 | 0.1382 |
| 11 | 0.125 | 3.175 | 0.1196 | 0.1233 |
| 12 | 0.1094 | 2.77876 | 0.1046 | 0.1084 |
| 13 | 0.0937 | 2.37998 | 0.0897 | 0.0934 |
| 14 | 0.0781 | 1.98374 | 0.0747 | 0.0785 |
| 15 | 0.0703 | 1.78562 | 0.0673 | 0.071 |
| 16 | 0.0625 | 1.5875 | 0.0598 | 0.0635 |
| 17 | 0.0562 | 1.42748 | 0.0538 | 0.0575 |
| 18 | 0.05 | 1.27 | 0.0478 | 0.0516 |
| 19 | 0.0437 | 1.10998 | 0.0418 | 0.0456 |
| 20 | 0.0375 | 0.9525 | 0.0359 | 0.0396 |
| 21 | 0.0344 | 0.87376 | 0.0329 | 0.0366 |
| 22 | 0.0312 | 0.79248 | 0.0299 | 0.0336 |
| 23 | 0.0281 | 0.71374 | 0.0269 | 0.0306 |
| 24 | 0.025 | 0.635 | 0.0239 | 0.0276 |
| 25 | 0.0219 | 0.55626 | 0.0209 | 0.0247 |
Chemical Composition:
| Grade | C | Si | Mn | P | S | Ni | Cr | Mo |
| 304 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.00～10.00 | 18.00～20.00 | - |
| 304L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 9.00～13.00 | 18.00～20.00 | - |
Physical Property:
| Grade | Tensile Strength(Mpa) | Yield Strength(Mpa) | Elongation(%) | HBW | HRB | HV |
| 304 | ≥520 | ≥205 | ≥40 | ≤187 | ≤90 | ≤200 |
| 304L | ≥480 | ≥175 | ≥40 | ≤187 | ≤90 | ≤200 |
304 VS 304L:
Grade 304L has a slight, but noticeable, reduction in key
mechanical performance characteristics compared to the “standard”
grade 304 stainless steel alloy.
For example, the ultimate tensile strength (UTS) of 304L is roughly
85 ksi (~586 MPa), less than the UTS of standard grade 304
stainless, which is 90 ksi (~620 MPa). The difference in yield
strength is slightly greater, with 304 SS having a 0.2% yield
strength of 42 ksi (~289 MPa) and 304L having a 0.2% yield strength
of 35 ksi (~241 MPa).
This means that if you had two steel wire baskets and both baskets
had the exact same design, wire thickness, and construction, the
basket made from 304L would be structurally weaker than the
standard 304 basket.
Surface Finish:
| Surface Finish | Definition | Application |
| 2B | Finished by heat treatment, pickling after cold rolling. Followed
by skin pass line to be more brighter and smooth surface | General application Medical instruments, Tableware |
| BA | Bright heat treament after cold rolling | Kitchen utensil, kitchenware, architectural |
| 8K | A mirror-like reflective surface by polishing with finer abrasives
over 800mesh | Construction, mirrors, plate sets, decoration elevators |
| HL | Finished by continuous linear polishing | Architectural purpose, Escalators, kitchenware, vehicles |
| NO.1 | Finished by hot rolling, annealing and picking, characterized by
white pickled surface | Chemical industry Equipment, industrail tanks |
| NO.4 | Polishing with NO.150 to NO.180 mesh abrasives specified in
JISR6001 | Kitchen utensils, Building Construction, Medical equipment |
Packing:
304 NO.1 Finish Stainless Steel Plate size 4x1500x6000 HR Sheet Packing 2 types:
l Standard packing
l Fine packing
Factory and Machine Equipment:
We had our own factory to do slitting re-rolling and finish
treatment machine,PVC and interleaving paper we will using with our
machine for you,could protect stainless steel surface from damage
or any scratches,
1. CNC Flame Cutting Machine
2. CNC Plasma Cutting Machine
3. CNC Laser Cutting Machine
4. Bending Machine
5. Shearing Machine
6. Punch Machine
7. Driving Machine
304 NO.1 Finish Stainless Steel Plate size 4x1500x6000 HR Sheet Diaplay:
WHY CHOOSE US:
Q1: What is your terms of payment?
A: 30% T/T in advance, the balance 70% before delivery. We will
show you the photos of products and package before you pay the
balance.
Q2: what is the terms of delivery?
A: FOB, CIF, CFR,
Q3: What is the terms of packing?
A: generally, we pack our goods in bundles or coils with rods or
belts, we could also pack the goods as the customers' requirement.
Q4: What is your delivery time?
A: For stocks, we could transport the goods to loading port within
7 days after we received your deposit.
For production period, it usually takes about 15 days-30 days after
receiving the deposit.
Q5: Could you produce according to the samples?
A : Yes, we could customer-made by your samples or technique
drawings, we could build the mold and fixtures.
Q6: Could you provide the samples?
A: yes, we could provide the free samples on conditons it is
available in stocks, however, the the transportation fee is borne
by buyer.